Productum Descriptio
Resinae Lepidium sativum	PA66 MoS₂ PTFE materia composita - iniectio gradus coronae, summus fluxus, auto-luctans, obsistens
Color	Tenebris griseo/nigris
Praecipua applicationes	Partes, anni, sigilla, sphockets, clausurae lavatores, partes valvae, ligamenta gerunt, applicationes autocinetas, applicationes electricas et electronicas, supellectilis, applicationes humilium strepitus, applicationes roboticas
Processususus Ratio	Iniectio CUMATIUM
Typical Properties	Test Methodus	Test Conditio	Precium	Unitas
Corporalis Propertie s
Density	DIN EN ISO 1183	23℃	1.24	g/cm³
DECREMENTUM	GB 15585		0.8-1.2	%
Mechanica Properties
distrahentes Fortitudo	DIN EN ISO 527	50mm/min	95	MPa
Modulus distrahens			4300	MPa
Elongation at Break			4.7	%
Flexurae Fortitudo	DIN EN ISO 178	2mm/min	123	MPa
Flexurale Modulus	DIN EN ISO 178	2mm/min	3900	MPa
Izod Notched Impact virtus	DIN EN ISO 180	4mm,23℃	6	KJ/M²
Izod Notched Impact virtus	DIN EN ISO 180	4mm, 30℃	4	KJ/M²
I zod Notched Impact virtus	DIN EN ISO 180	4mm,23℃	115	KJ/M²
I zod Notched Impact virtus	DIN EN ISO 180	4mm, 30℃	80	KJ/M²
Frictio Coefficientis	ASTM D3702	Dynamie VS Steel	0.2
Frictio Coefficientis	ASTM D3702	Static VS Steel	0.26
Frictio Coefficientis	ASTM D3702	elementum	35	ft-1b-hr
Scelerisque Euismod
Calor Deformatio Temperature	DIN EN ISO 75	1.8 MPa, inannealed	87	℃
Calor Deformatio Temperature	DIN ENISO 75	0.45 MPa, inannealed	240	℃
Retardantia flammea possessiones
Retardantia flammea properties	UL94	0.75	HB
Retardantia flammea properties	UL94	1.5mm	HB
Retardantia flammea properties	UL94	3mm	HB
alii
Superficies resistivity	IEC60093	1.5mm	10¹3-15	Ω

"Nota: (1) Notitia provisa sunt valores typici ac solum ut relatio ad clientium intenditur, nec cautionem constituunt signa minima vel maxima qualitatis, nec in fideiussoribus aliud finem faciunt.
(2) euismod variari potest secundum colorem.
"Cautio: Notitia et notitia quae in hac nostra scientia et experientia fundantur. Si nova cognitio vel experientia in futurum praesto fiant, ius reservamus emendandi informationes et notitias in hoc documento sine praevia notatione. Condiciones usus et applicabiles leges variari possunt loco et tempore, emptoris est responsabilitas statuere an producta et producta notitia in his contenta sint usui eorum apta, et ut eorum opera et rationes novarum rationum administrandi. nullam obligationem vel obligationem assumit in relatione ad informationes in hoc contentas, nec aliquam praestat warantum.

Typical Iniectio CUMATIUM Process
Plastic Siccatio
Siccatio Time	2～4h
Siccatio Temperature	100～130℃
Siccatio Equipment	Hot-aer dryer
Siccatio Type	Continua remittit (production process)
Iniectio CUMATIUM Process
COLLUM Sectio	270～290℃
Plastics Sectio	280～ 300℃
Deportatio Sectionis	260～280℃
Maximum Iniectio Temperature	330℃
Iniectio Pressure	40～120MPa
Iniectio Speed	30～75mm/s
Plasticization Pressura Velocitas	Pressura: 65-100 MPa; Celeritas: 60-85 mm/s
Plasticization Back Pressura	10～40MPa
Forma Commendatur Temperature	80～100℃

Frictio et gere, euismod
Haec materia humilem frictionem coefficiens praebet, sicut PTFE signanter frictionem superficiem reducit et excellentem sui lubricationem praebet. Eodem tempore, praestantes induti resistentia conservat, ex infima rate et extenso usu vitae. Vulgo usus est in partibus lapsibus sicut gestus olei gratuiti, cancellos labens, et cancellos ducere.

Mechanica Properties
Materia altam vim et rigorem retinet plasticae machinalis PA66 propriae, sinit eam onera relative alta sustinere. Additio MoS₂ etiam auget stabilitatem scelerisque, stabilitatem dimensionalem et calorem resistentem sub elevatis temperaturis emendans. Applicationes typicas includunt onera portantes componentes ut cams mechanicas, apparatum olei partes, machinam autocineticam, et partes sparguntur.

Aliquam euismod
Bonam stabilitatem dimensivam ostendit ob effusio et DECREMENTUM umoris relative humilis, certa praecisio in complexibus ambitibus praestans. Praeterea validam resistentiam habet amplis chemicis, menstrua et oleis. Inde idoneus facit ad praecisionem partium transmissionis sicut anni (incluso motore et instrumento instrumenti) et caveis ferendis, tum componentibus industrialibus ut partes machinis textilibus (exampla, shuttles et tincta duces) et interna in officio instrumenti automationis.

Technical SAGACITAS et Application Praecipua
Materia utilitates ex effectu synergistico: PA66 praecipuas vires et calor resistentia praebet, dum MoS₂ et PTFE funguntur solidi lubricantes. PTFE translationem pellicularum in superficiebus contactis format ad frictionem reducendam, MoS' autem duritiem meliorem facit et resistentiam adhibet. Haec coniunctio efficit materiam maxime efficacem in celeritate, magno onere, vel applicationibus difficilibus sustentationem.

Secundum processus, haec mutatio materiae typice fabricata est utens iniectio fingens. Cum PA66 hygroscopicum sit, penitus exsiccari oportet antequam processus (exempli gratia in 100°C per 4 horas circiter) ne vitia qualia sunt bullae vel degradatio materialis, ita ut optimam perficiant finalem.